【Products】Rutile Titanium Dioxide(R288)
 
【Product detail】

Yuanjiang Brand titanium dioxide R288  is produced by sulfuric acid process is a kind of rutile type titanium dioxide. Zirconia, silicon and aluminium ternary composite inorganic surface treatment, with special organic processing agent for surface modification and has a blue phase, easy dispersion, high weatherability, high covering power, low oil absorption, good system compatibility and excellent processing rheological characteristics, is a partial oily, high-quality plastic special titanium dioxide. Can be widely used in polyolefin, PVC, ABS, PS masterbatch, profiles, sheet, pipe, and can also be used for leather color paste, oil paint.

Technical index

Item Index
Titanium Dioxide contect, % ≥95
Brightness content, % ≥98
Whiteness, %

Not less than

Tinting strength,compared with the standard sample ≥96
Matter volatile at 105ºC, % ≤1.0

Water soluble matter, %

≤0.3

PH of aqueous suspension

6.5-8.0
Oil absorption, g/ 100g ≤23
Residue on sieve 45µm, % ≤0.1
Resistivity of aqueous extract , Ω.cm ≥8000

Application characteristics

At the end of the blue phaser288 average particle size is close to the scattering of blue light in titanium dioxide theory the optimum particle diameter, small particle size of TiO2 is higher than that of large particle diameter is more effective, so it has more blue bottom and excellent whiteness. 
Excellent dispersionspecial inorganic surface treatment and organic surface treatment to reduce the contact between the TiO2 particles, so that R288 in the application process showed excellent dispersion. So good wettability, easy to grind. 
Low oilR288 low oil, titanium dioxide to maintain good processing performance in the application process in the plastic. 
High weather resistanceR288 using zirconium coating treatment process to improve the weather resistance and heat resistance of titanium dioxide, and thus the chemical properties are very stable.
Good system compatibilityR288 special organic surface treatment, is very suitable for the non polar system and oily system, so in the application showed good system compatibility. 
Packing:25 kg plastic woven bag for mixed bag or 500, 1000 kg of plastic.
Product storageas long as avoid damp, can be long-term storage.